- briquetting pressure
- forming pressure
- "成型"英文翻译 shaping; forming
- "压力"英文翻译 pressure; tension
- "轮毂成型压力机" 英文翻译 : hub punch press
- "粉末金属成型压力机" 英文翻译 : powder metal moulding press
- "成型压板" 英文翻译 : contoured squeeze board
- "成型压实" 英文翻译 : contour squeeze
- "成型压头" 英文翻译 : contoured squeeze board
- "成型压制机" 英文翻译 : compacting press
- "注塑成型压机" 英文翻译 : injection molding press; injection press
- "u型压力表" 英文翻译 : u-gage; u-gauge
- "u型压力计" 英文翻译 : u gauge; u-gauge
- "型压力计" 英文翻译 : u-gauge
- "型压力接头" 英文翻译 : flow cross t
- "造型压力" 英文翻译 : molding pressure
- "钟型压力计" 英文翻译 : bell pre ure gage; bell pressure gage; bell type manometer
- "重型压力机" 英文翻译 : heavy duty press; heavy-duty press; super compactor
- "波登型压力计" 英文翻译 : bourdontype pressure gauge
- "大型压力容器" 英文翻译 : large pressurized vessel
- "底重型压力表" 英文翻译 : deadweight gauge
- "型压力溶气罐" 英文翻译 : rg type pressure dissolved air pot; tr type pressure dissolved gas pot
- "翼型压力分布" 英文翻译 : airfoil pressure distribution; profile pressure distribution
- "翼型压力中心" 英文翻译 : airfoil center of pressure
- "滑动成型压砖机" 英文翻译 : sliding mold type press; sliding mould type press; sliding mould-type press
- "小型压力传感器" 英文翻译 : miniature pressure cell
- "新型压力管反应堆" 英文翻译 : advanced pressure tube reactor; aptr
例句与用法
- The optimal molding temperature and pressure of their composite are 140c and 7 . 3 mpa
麻纤维复合材料的最佳成型温度为140 ,成型压力7 . 3mpa 。 - When compressing , the proper pressure is between 7 - 11 t / cm2 , the keeping time is 60s or so
磁体压制时合适的成型压力在7 11t cm ~ 2之间,合适的保压时间在60s左右。 - It was found that the compression speed and compression stroke are the two factors affecting the molding pressure most significantly
由模拟找出了压缩速度与压缩行程是两个影响成型压力极大的因素。 - It was found that the compression speed and compression stroke are the two factors affecting the molding pressure most significantly
由仿真找出了压缩速度与压缩行程是两个影响成型压力极大的因素。 - In order to meet the need of production in practice , the proper molding water content , pressure and curing age were determined by experiment and analysis
结合现场的生产要求,通过大量实验与分析,给出了合理的成型加水量、成型压力和养护龄期。 - The experiment results show that the reduction by carbon and nitridation is connected with the reaction temperature , molding pressure and ratio of tio2 / c of the sample
实验结果表明:制备试样的成型压力、材料本身的tio _ 2 c比、氮化温度对氮化率有一定影响。 - As shown by the measurements , the electrical resistivity of sintered psc has a tendency of first decreasing and then increasing as the sintering temperature and / or sintering time increase . also it decreases with the increased pressure on the pressed powder compact
对样品的电阻率进行了测量,总体呈现出随烧结时间和烧结温度的增加而先降低后增加的趋势,并随压坯的成型压力的增加而降低。 - The bonded magnets with excellent magnetic properties were manufactured by wetly - mixed epoxy and prfeb powders , which granularity was 100 to 140 , and under the pressure of 600 to 800 mpa . then the magnets were solidified 2 hours , under the temperature of 160c
结果表明,当环氧树脂与磁粉采用溶剂湿混,成型压力选为600 ? 800mpa ,磁粉颗粒在100 ? 140目之间,磁体在160 ~ c真空固化2小时,粘结prfeb永磁合金的磁性能达到最佳。 - 3 . based on the gel time and dsc curve figure of two kinds of modified phenolic resin and flory and kissinger theory , the rage of cure process parameters for the resin system , moulding pressure and resin content are established
3 、通过对二种改性酚醛树脂体系凝胶时间、 dsc曲线图的分析,引入flory理论、 kissinger理论,确定了树脂体系的固化工艺参数(固化温度、固化时间、后处理温度)范围;并初步确定了成型压力和树脂含量的范围。 - 4 . the optimistic resin system and the effect of resin content on the targets performance are discussed by orthogonal experiments , based on which , the moulding process parameters such as temperature , pressure , cycle and post - cure temperature are designed optimistically
4 、通过正交试验确定了最佳树脂体系,确定了含胶量对靶板性能的影响,在选定基体材料基础上,通过正交试验分析,对复合材料成型工艺参数如:成型温度、成型压力、成型时间、后处理温度进行了优化设计,确定了体系的最佳成型工艺参数。
- 更多例句: 1 2